高剛性PC EGN-2010R2

 Iupilon/NOVAREX/XANTAR are well known polycarbonate resin in the market for many years. Used in a wide range of industries, including sports equipment, medical equipment, automobiles, optics, machinery, office automation equipment, and electronics, they have a reputation for reliability with users. In addition, Mitsubishi Engineering-Plastics backs up them with superior Product Information and an abundance of application data.

Iupilon/NOVAREX/XANTAR是三菱工程塑料株式會社研究開發(fā)成功的聚碳酸酯，在市場上已有好多年歷史。 被廣泛地用于各種工業(yè)生產(chǎn)，如運(yùn)動器械、醫(yī)療器械、汽車部件、光學(xué)儀器、機(jī)械、辦公自動化設(shè)備和電子設(shè)備，獲得了客戶的廣泛信賴和支持。 三菱工程塑料株式會社以自身力量研發(fā)成功的同時(shí)更提供了高端的技術(shù)服務(wù)和豐富產(chǎn)品技術(shù)資料。

Special features:

• Superior impact strength

• Superior transparency

• Usability in a wide range of temperatures: -40degC to 120degC

• Excellent precision molding properties and dimensional stability

• Superior self-extinguishing properties

• Excellent weather resistance

• Excellent electrical insulation capabilities

特點(diǎn)：

·         耐沖擊性佳

·         高度透明性

·         使用溫度范圍廣： -40到160

·         精密成形性能佳、成型尺寸穩(wěn)定

·         超高自熄性能

·         超耐候性

·         電氣絕緣特性佳

高剛性PC EGN-2010R2

Iupilon/Novarex 的耐疲勞特性，呈現(xiàn)如圖 3.8.1-1，2，3，4 所示那樣的性能（測定法為定負(fù)荷 1000cycle/min 室溫）。圖 3.8.1-1 為拉伸壓縮疲勞隨試驗(yàn)片形狀的變化。很明顯形狀對性能有很大影響，特別是切削加工的試樣，切削的影響十分巨大。圖 3.8.1-2 為拉伸壓縮疲勞的結(jié)果，圖 3.8.1-3 為彎曲疲勞的結(jié)果，圖 3.8.1-4 為扭轉(zhuǎn)疲勞的結(jié)果。無論那個(gè)試驗(yàn)，分子量增加的情況下，材料的耐疲勞性都得到了改善?；剞D(zhuǎn)彎曲疲勞（試驗(yàn)片為切削加工制作）時(shí)溫度的影響如圖 3.8.1-5 所示。溫度低的情況下，疲勞界限會有一個(gè)大幅的提高。